Carbon steel English www.tool-tool.com


Bewise Inc. www.tool-tool.com Reference source from the internet.

v d e
Iron alloy phases

Austenite (γ-iron; hard)
Bainite
Martensite
Cementite (iron carbide; Fe3C)
Ledeburite (ferrite - cementite eutectic, 4.3% carbon)
Ferrite (α-iron, δ-iron; soft)
Pearlite (88% ferrite, 12% cementite)
Spheroidite

Types of steel

Carbon steel (≤2.1% carbon; low alloy)
Stainless steel (steel with chromium)
HSLA steel (high strength low alloy)
Tool steel (very hard)

Other iron-based materials

Cast iron (>2.1% carbon)
Wrought iron (contains slag)
Ductile iron


Carbon steel, also called plain carbon steel, is a metal alloy, a combination of two elements, iron and carbon, where other elements are present in quantities too small to affect the properties. The only other alloying elements allowed in plain-carbon steel are manganese (1.65% max), silicon (0.60% max), and copper (0.60% max).[1] Steel with a low carbon content has the same properties as iron, soft but easily formed. As carbon content rises, the metal becomes harder and stronger but less ductile and more difficult to weld. Higher carbon content lowers steel's melting point and its temperature resistance in general.

Carbon content influences the yield strength of steel because carbon molecules fit into the interstitial crystal lattice sites of the body-centered cubic arrangement of the iron molecules. The interstitial carbon reduces the mobility of dislocations, which in turn has a hardening effect on the iron. To get dislocations to move, a high enough stress level must be applied in order for the dislocations to "break away". This is because the interstitial carbon atoms cause some of the iron BCC lattice cells to distort.

[edit] Types of carbon steel

Typical compositions of carbon:

  • Mild (low carbon) steel: approximately 0.05–0.15% carbon content for low carbon steel and 0.16-0.29% carbon content for mild steel[2] (e.g. AISI 1018 steel). Mild steel has a relatively low tensile strength, but it is cheap and malleable; surface hardness can be increased through carburizing.[3]
  • Medium carbon steel: approximately 0.30–0.59% carbon content[2](e.g. AISI 1040 steel). Balances ductility and strength and has good wear resistance; used for large parts, forging and automotive components.[4]
  • High carbon steel: approximately 0.6–0.99% carbon content [2]. Very strong, used for springs and high-strength wires.[5]
  • Ultra-high carbon steel: approximately 1.0–2.0% carbon content [2]. Steels that can be tempered to great hardness. Used for special purposes like (non-industrial-purpose) knives, axles or punches. Most steels with more than 1.2% carbon content are made using powder metallurgy and usually fall in the category of high alloy carbon steels.

Steel can be heat-treated which allows parts to be fabricated in an easily-formable soft state. If enough carbon is present, the alloy can be hardened to increase strength, wear, and impact resistance. Steels are often wrought by cold-working methods, which is the shaping of metal through deformation at a low equilibrium or metastable temperature.

[edit] Metallurgy

Mild steel is the most common form of steel as its price is relatively low while it provides material properties that are acceptable for many applications. Mild steel has a low carbon content (up to 0.3%) and is therefore neither extremely brittle nor ductile. It becomes malleable when heated, and so can be forged. It is also often used where large amounts of steel need to be formed, for example as structural steel. Density of this metal is 7,861.093 kg/m³ (0.284 lb/in³), the tensile strength is a maximum of 500 MPa (72,500 psi) and it has a Young's modulus of 210 GPa.

Carbon steels which can successfully undergo heat-treatment have a carbon content in the range of 0.30–1.70% by weight. Trace impurities of various other elements can have a significant effect on the quality of the resulting steel. Trace amounts of sulfur in particular make the steel red-short. Low alloy carbon steel, such as A36 grade, contains about 0.05% sulfur and melts around 1426–1538 °C (2600–2800 °F).[6] Manganese is often added to improve the hardenability of low carbon steels. These additions turn the material into a low alloy steel by some definitions, but AISI's definition of carbon steel allows up to 1.65% manganese by weight.

Hardened steel usually refers to quenched or quenched and tempered steel.

Silver steel or high-carbon bright steel gets its name from its appearance. It is a very-high carbon steel. It is defined under the steel specification standards BS-1407. It is a 1%-carbon tool steel which can be ground to close tolerances. Usually the range of carbon is in the range 1.10% - 1.20%. It also contains trace elements of 0.35% Mn (range 0.30–0.40%), 0.40% Cr (range 0.4–0.5%), 0.30% Si (range 0.1–0.3%), and also sometimes sulfur (max 0.035%) and phosphorus (max 0.035%). Silver steel is sometimes used for making straight razors, due to its ability to produce and hold a micro-fine edge.

[edit] Heat treatments

Iron-carbon phase diagram, showing the temperature and carbon ranges for certain types of heat treatments.

Iron-carbon phase diagram, showing the temperature and carbon ranges for certain types of heat treatments.

The purpose of heat treating carbon steel is to change the mechanical properties of steel, usually ductility, hardness, yield strength, and impact resistance. Note that the electrical and thermal conductivity are slightly altered. As with most strengthening techniques for steel, the modulus of elasticity (Young's modulus) is never affected. Steel has a higher solid solubility for carbon in the austenite phase, therefore all heat treatments, except spheroidizing and process annealing, start by heating to an austenitic phase. The rate at which the steel is cooled through the eutectoid reaction affects the rate at which carbon diffuses out of austenite. Generally speaking, cooling quickly will give a finer pearlite (until the martensite critical temperature is reached) and cooling slowly will give a coarser pearlite. Cooling a hypoeutectoid (less than 0.77 wt% C) steel results in a pearlitic structure with α-ferrite at the grain boundaries. If it is hypereutectoid (more than 0.77 wt% C) steel then the structure is full pearlite with small grains of cementite scattered throughout. The relative amounts of constituents are found using the lever rule. Here is a list of the types of heat treatments possible:

  • Spheroidizing: Spheroidite forms when carbon steel is heated to approximately 700 °C for over 30 hours. Spheroidite can form at lower temperatures but the time needed drastically increases, as this is a diffusion controlled process. The result is a structure of rods or spheres of cementite within primary structure (ferrite or pearlite, depending on which side of the eutectoid you are on). The purpose is to soften higher carbon steels and allow more formability. This is the softest and most ductile form of steel. The image to the right shows where spheroidizing usually occurs.[7]
  • Full annealing: Carbon steel is heated to approximately 40 °C above Ac3 or Ac1 for 1 hour; this assures all the ferrite transforms into austenite (although cementite might still exist if the carbon content is greater than the eutectoid). The steel must then be cooled slowly, in the realm of 38 °C (100 °F) per hour. Usually it is just furnace cooled, where the furnace is turned off with the steel still inside. This results in a coarse pearlitic °structure, which means the "bands" of pearlite are thick. Fully annealed steel is soft and ductile, with no internal stresses, which is often necessary for cost-effective forming. Only spheroidized steel is softer and more ductile.[8]
  • Process annealing: A process used to relieve stress in a cold-worked carbon steel with less than 0.3 wt% C. The steel is usually heated up to 550–650 °C for 1 hour, but sometimes temperatures as high as 700 °C. The image to the right shows the area where process annealing occurs.
  • Isothermal annealing: It is a process in which hypoeutectoid steel is heated above the upper critical temperature and this temperature is maintained for a period of time and then the temperature is brought down below lower critical temperature and is again maintained. Then finally it is cooled at room temperature. This method helps in eliminating any temperature gradient.
  • Normalizing: Carbon steel is heated to approximately 55 °C above Ac3 or Acm for 1 hour; this assures the steel completely transforms to austenite. The steel is then air cooled, which is a cooling rate of approximately 38 °C (100 °F) per minute. This results in a fine pearlitic structure, and a more uniform structure. Normalized steel has a higher strength than annealed steel; it has a relatively high strength and ductility.[9]
  • Quenching: Carbon steel with at least 0.4 wt% C is heated to normalizing temperatures and then rapidly cooled (quenched) in water, brine, or oil to the critical temperature. The critical temperature is dependent on the carbon content, but as a general rule is lower as the carbon content increases. This results in a martensitic structure; a form of steel that possesses a super-saturated carbon content in a deformed body-centered cubic (BCC) crystalline structure, properly termed body-centered tetragonal (BCT). This crystalline structure has a very high amount of internal stress. Due to these internal stress quenched steel is extremely hard but brittle, usually too brittle for practical purposes. These internal stresses cause stress cracks on the surface. Quenched steel is approximately three (lower carbon content) to four (high carbon content) times harder than normalized steel.[10]
  • Martempering (Marquenching): Martempering is not actually a tempering procedure, hence the term "Marquenching." It is a form of isothermal heat treatment applied after an initial quench of typically in an oil or brine solution at a temperature right above the "martensite start temperature". At this temperature, residual stresses within the material are relieved and some bainite may be formed from the retained ferrite which did not have time to transform into anything else. In industry, this is a process used to control the ductility and hardness of a material. With longer marquenching time, the ductility increases with a minimal loss in strength; the steel is held in this solution until the center and surface temperatures equalize. Then the steel is cooled at a moderate speed to keep the temperature gradient minimal. Not only does this process reduce internal stresses and stress cracks, but it also increases the impact resistance.[11]
  • Quench and tempering: This is the most common heat treatment encountered, because the final properties can be precisely determined by the temperature and time of the tempering. Tempering involves reheating quenched steel to a temperature below the eutectoid temperature then cooling. The elevated temperature allows very small amounts of spheroidite to form, which restore ductility, but reduces hardness. Actual temperatures and times are carefully chosen for each composition.[12]
  • Austempering: The austempering process is the same as martempering, except the steel is held in the brine solution through the bainite transformation temperatures, and then moderately cooled. The resulting bainite steel has a greater ductility, higher impact resistance, and less distortion. The disadvantage of austempering is it can only be used on a few steels, and it requires a special brine solution.[13]

[edit] Case hardening

Only the exterior of the steel part is hardened, creating a hard, wear resistant skin, but preserving a tough and ductile interior.

A limitation of plain carbon steel is the very rapid rate of cooling needed to produce hardening. In large pieces it is not possible to cool the inside rapidly enough and so only the surfaces can be hardened. This can be improved with the addition of other elements resulting in alloy steel.

[edit] Flame and induction hardening

Induction heating is when the surface of the steel is heated to high temperatures then cooled rapidly through the use of localized heating mechanisms and water cooling. The purpose is to create a "case" of martensite on the surface where wear resistance is needed. A carbon content of 0.4–0.6 wt% C is needed for this type of hardening. Typical uses are for the shackle of a lock, where the outer layer is hardened to be file resistant, and mechanical gears where hard gear mesh surfaces are needed to maintain a long service life while toughness is required to maintain durability and resistance to catastrophic failure.

[edit] Carburizing

Main article: Carburization

A process used to case harden steel with a carbon content between 0.1 and 0.3 wt% C. In this process steel is introduced to a carbon rich environment and elevated temperatures for a certain amount of time. Because this is a diffusion controlled process, the longer the steel is held in this environment greater the carbon penetration will be and the higher the carbon content in these areas. The part is then quenched so that the carbon is locked in the structure. The hardness is moderately increased, but it can be hardened again through flame or induction hardening. It's possible to carburize only a portion of the part by covering it in copper plating or coating it with a commercial paste. The following are some examples of carburizing processes:[14]

  • Pack carburizing: Packing low carbon steel parts with a carbonaceous material and heating for some time diffuses carbon into the outer layers. A heating period of a few hours might form a high-carbon layer about one millimeter thick.
  • Liquid carburizing: This method involves heating the part in a bath of molten barium cyanide or sodium cyanide. The surface absorbs both sodium and carbon this way.[15]
  • Gas carburizing: Parts placed into a furnace at 927 °C (1700 °F) containing a partial methane or carbon monoxide atmosphere. The parts are then quenched.
  • Carburization may also be accomplished with an acetylene torch set with a fuel rich flame and heating and quenching repeatedly in a carbon rich fluid (oil).

[edit] Nitriding

Main article: Nitriding

This process heats the steel part to 482–621 °C (900–1150 °F) in an atmosphere of ammonia gas and dissociated ammonia. The time the part spends in this environment dictates the depth of the case. The hardness is achieved by the formation of nitrides. Nitride forming elements must be present for this method to work; these elements include chromium, molybdenum, and aluminium. The advantage of this process is it causes little distortion, so the part can be case hardened after being quench and tempered and machined.

[edit] Cyaniding

This is a casehardening process that is fast and efficient; it is mainly used on Low carbon steels. The part is heated to 1600-1750º F in a bath of sodium cyanide and then is quenched and rinsed, in water or oil, to remove any residual cyanide.

This process produces a thin, hard shell (0.010 in. and 0.030 in.) that is harder than the one produced by carburizing and can be completed in 20 to 30 minutes compared to several hours. Advantage of this method is the short time it requires to complete the diffusion; otherwise it should be avoided because of high distortion. The major drawback of Cyaniding is that cyanide salts are poisonous.

The Typical Applications of this process are Bolts, Nuts, Screws, and Small Gears.

[edit] Carbonitriding

Main article: Carbonitriding

This process is similar to cyaniding except a gaseous atmosphere of ammonia and hydrocarbons is used instead of sodium cyanide. If the part is to be quenched then the part is heated to 775–885 °C (1425–1625 °F); if not then the part is heated to 649–788 °C (1200–1450 °F). Trade names for the process include Tenifer, Melonite, Sursulf, Arcor, Tufftride, and Koline.

歡迎來到Bewise Inc.的世界,首先恭喜您來到這接受新的資訊讓產業更有競爭力,我們是提供專業刀具製造商,應對客戶高品質的刀具需求,我們可以協助客戶滿足您對產業的不同要求,我們有能力達到非常卓越的客戶需求品質,這是現有相關技術無法比擬的,我們成功的滿足了各行各業的要求,包括:精密HSS DIN切削刀具協助客戶設計刀具流程DIN or JIS 鎢鋼切削刀具設計NAS986 NAS965 NAS897 NAS937orNAS907 航太切削刀具,NAS航太刀具設計超高硬度的切削刀具BW捨棄式鑽石V卡刀BW捨棄式金屬圓鋸片木工捨棄式金屬圓鋸片PCD木工圓鋸片醫療配件刀具設計汽車業刀具設計電子產業鑽石刀具全鎢鋼V卡刀-電路版專用全鎢鋼鋸片焊刃式側銑刀焊刃式千鳥側銑刀焊刃式T型銑刀焊刃式千鳥T型銑刀焊刃式螺旋機械鉸刀全鎢鋼斜邊刀電路版專用鎢鋼焊刃式高速鉸刀超微粒鎢鋼機械鉸刀超微粒鎢鋼定點鑽焊刃式帶柄角度銑刀焊刃式螺旋立銑刀焊刃式帶柄倒角銑刀焊刃式角度銑刀焊刃式筒型平面銑刀木工產業鑽石刀具等等。我們的產品涵蓋了從民生刀具到工業級的刀具設計;從微細刀具到大型刀具;從小型生產到大型量產;全自動整合;我們的技術可提供您連續生產的效能,我們整體的服務及卓越的技術,恭迎您親自體驗!!

BW Bewise Inc. Willy Chen willy@tool-tool.com bw@tool-tool.com www.tool-tool.com skype:willy_chen_bw mobile:0937-618-190 Head &Administration Office No.13,Shiang Shang 2nd St., West Chiu Taichung,Taiwan 40356 http://www.tool-tool..com / FAX:+886 4 2471 4839 N.Branch 5F,No.460,Fu Shin North Rd.,Taipei,Taiwan S.Branch No.24,Sec.1,Chia Pu East Rd.,Taipao City,Chiayi Hsien,Taiwan

Welcome to BW tool world! We are an experienced tool maker specialized in cutting tools. We focus on what you need and endeavor to research the best cutter to satisfy users demand. Our customers involve wide range of industries, like mold & die, aerospace, electronic, machinery, etc. We are professional expert in cutting field. We would like to solve every problem from you. Please feel free to contact us, its our pleasure to serve for you. BW product including: cutting toolaerospace tool .HSS DIN Cutting toolCarbide end millsCarbide cutting toolNAS Cutting toolNAS986 NAS965 NAS897 NAS937orNAS907 Cutting Tools,Carbide end milldisc milling cutter,Aerospace cutting toolhss drillФрезерыCarbide drillHigh speed steelMilling cutterCVDD(Chemical Vapor Deposition Diamond )’PCBN (Polycrystalline Cubic Boron Nitride) Core drillTapered end millsCVD Diamond Tools Inserts’PCD Edge-Beveling Cutter(Golden FingerEdge modifying knifeSolid carbide saw blade-V typeV-type locking-special use for PC boardMetal Slitting SawaCarbide Side milling CuttersCarbide Side Milling Cutters With Staggered TeethCarbide T-Slot Milling CuttersCarbide T-Slot Milling Cutters With Staggered TeethCarbide Machine ReamersHigh speed reamer-standard typeHigh speed reamer-long type’’PCD V-CutterPCD Wood toolsPCD Cutting toolsPCD Circular Saw BladePVDD End Millsdiamond tool V-type locking-special use for PC board Single Crystal Diamond Metric end millsMiniature end millsСпециальные режущие инструментыПустотелое сверло Pilot reamerFraisesFresas con mango PCD (Polycrystalline diamond) ‘FreseElectronics cutterStep drillMetal cutting sawDouble margin drillGun barrelAngle milling cutterCarbide burrsCarbide tipped cutterChamfering toolIC card engraving cutterSide cutterNAS toolDIN or JIS toolSpecial toolMetal slitting sawsShell end millsSide and face milling cuttersSide chip clearance sawsLong end millsStub roughing end millsDovetail milling cuttersCarbide slot drillsCarbide torus cuttersAngel carbide end millsCarbide torus cuttersCarbide ball-nosed slot drillsMould cutterTool manufacturer.

Bewise Inc. www.tool-tool.com

ようこそBewise Inc.の世界へお越し下さいませ、先ず御目出度たいのは新たな

情報を受け取って頂き、もっと各産業に競争力プラス展開。

弊社は専門なエンドミルの製造メーカーで、客先に色んな分野のニーズ

豊富なパリエーションを満足させ、特にハイテク品質要求にサポート致します。

弊社は各領域に供給できる内容は:

(1)精密HSSエンドミルのR&D

(2)Carbide Cutting tools設計

(3)鎢鋼エンドミル設計

(4)航空エンドミル設計

(5)超高硬度エンドミル

(6)ダイヤモンドエンドミル

(7)医療用品エンドミル設計

(8)自動車部品&材料加工向けエンドミル設計

弊社の製品の供給調達機能は:

(1)生活産業~ハイテク工業までのエンドミル設計

(2)ミクロエンドミル~大型エンドミル供給

(3)小Lot生産~大量発注対応供給

(4)オートメーション整備調達

(5)スポット対応~流れ生産対応

弊社の全般供給体制及び技術自慢の総合専門製造メーカーに貴方のご体験を御待ちしております。

BW специализируется в научных исследованиях и разработках, и снабжаем самым высокотехнологичным карбидовым материалом для поставки режущих / фрезеровочных инструментов для почвы, воздушного пространства и электронной индустрии. В нашу основную продукцию входит твердый карбид / быстрорежущая сталь, а также двигатели, микроэлектрические дрели, IC картонорезальные машины, фрезы для гравирования, режущие пилы, фрезеры-расширители, фрезеры-расширители с резцом, дрели, резаки форм для шлицевого вала / звездочки роликовой цепи, и специальные нано инструменты. Пожалуйста, посетите сайт www.tool-tool.com для получения большей информации.

BW is specialized in R&D and sourcing the most advanced carbide material with high-tech coating to supply cutting / milling tool for mould & die, aero space and electronic industry. Our main products include solid carbide / HSS end mills, micro electronic drill, IC card cutter, engraving cutter, shell end mills, cutting saw, reamer, thread reamer, leading drill, involute gear cutter for spur wheel, rack and worm milling cutter, thread milling cutter, form cutters for spline shaft/roller chain sprocket, and special tool, with nano grade. Please visit our web www.tool-tool.com for more info.

No comments: